The Fe/Mo ordering at B?sites of Ba₂FeMoO_6-δ (BFM) were changed by adjusting Fe/Mo amount of substance ratio (i.e., stoichiometric ratio), and then a new double?perovskite anode material Ba₂Fe_1.3Mo_0.7O_6-δ (BFM_0.7) for SOFC were obtained. The results indicated that the electrical conductivity of the BFM_0.7 anode is 15.0~20.0 S/cm at 600~800 ℃ in H₂, which is much larger than that of the lowest target for SOFC electrode (0.1 S/cm). The peak power density and polarization resistance of the BFM_0.7 anode cell attained 1 149 mW/cm² and 0.15 Ω·cm² at 850 ℃. Compared with BFM anode, the performance of BFM_0.7 is significantly improved. In addition, the performance of BFM_0.7 anode cell showed no degradation after testing for 39 h, indicating that the BFM_0.7 anode possesses has excellent electrochemical stability.